| GTD 241 Alloy High Lights | |
|---|---|
| Heat Treatment |
|
| Density | 8.3 g/cm³ |
| Common commercial designation | GTD-241 |
| Typical users | Gas turbine OEMs (nozzles, stationary components), repair shops |
| Forms |
|
| Maximum Service Temperature | Up to ~980-1050°C |
|
Get GTD 241 Alloy as per Standards Click Here |
|
Table of Content
GTD-241 Nickel-Based Superalloy Supplier in India, Check Density
| Property | Value |
|---|---|
| Dencity | 8.4 g/cm³. |
- Excellent High-Temperature Strength
- Superior Oxidation Resistance
- Enhanced Creep-Rupture Life
- High Fatigue Resistance
- Good Hot Corrosion Resistance
- Good Castability
Buy GTD 241 Alloy With Approximately 22.5% Chromium, 19% Cobalt, Refer Composition
| Alloy Name | AI | B | C | Nb | Co | Cr | Fe | Mn | Mo | Ni | Si | Ta | Ti | W | ZR | Others |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| GTD241 | 1.20 | 0.004 | 0.10 | 19.0 | 22.5 | - | - | - | Bal | - | - | 2.3 | 2.0 | 0.01 | Nb+0.508Ta 1.3 |
| Property | Value |
|---|---|
| 0.2% Proof (yield) strength, RT | ~ 600 - 1000 MPa |
| Ultimate tensile strength (UTS), RT | ~ 800 - 1200 MPa |
| Elongation (A%), RT | ~ 3 - 12 % (typical/range) |
| Hardness (approx.) | HRC: ~35-45 (or HV ~350-500) |
| Property | Value |
|---|---|
| Density | ≈ 8.3 - 8.5 g/cm³ |
| Melting / solidus range (approx.) | ≈ 1250 - 1350 °C (solidus/liquidus depend on exact composition) |
| Elastic modulus (E), RT | ≈ 200 - 220 GPa |
Stockist Of High-Temperature Strength GTD 241 Material in Mumbai Suitable For Application like Gas Turbines
| Heat Treatment | |
|---|---|
| Solution Treatment | 1120-1180°C |
| Air Cooling | Cooled in air after solution treatment |
| Aging Treatment | 760-870°C |
| Stress Relief | Performed at 870-980°C |
Offer GTD 241 Nickel and Cobalt based Superalloys in Various Forms like Round bar and Many More
- Round Bars
- Rods
- Cast Components
- Precision Investment Castings
- Blades & Vanes (Aerospace/Turbine)
Find GTD- 241 Developed By General Electric Produced via Specialized Casting Methods, See Equivalent Material
| Alloy Name | GE |
|---|---|
| GTD241 | B50A972 |
| - | °C | °F |
|---|---|---|
| Pre alloying | 1010° - 1040° C | 1850° - 1910° F |
| Casting | 935° - 955° C | 1715° - 1751° F |
| 920° - 940° C | 1688° - 1724° F | |
| Flask | 510° - 650° C | 950° - 1202° F |
- Vacuum Investment Casting
- Equiaxed Casting
- Directional Solidification Casting
- Single Crystal Casting
- Vacuum Melt + Airframe Casting
- Centrifugal Casting
- Precision Sand Casting
| Thermal Conductivity | ~10-14 W/m·K (at elevated temperatures) |
|---|---|
| Coefficient of Thermal Expansion (CTE) | ~13-15 µm/m·°C |
| Specific Heat Capacity | ~450-550 J/kg·K |