| In 625 Alloy High Lights |
| Standard Specifications |
- ASTM B443, ASTM B444, ASTM B446
- AMS 5599, AMS 5666
|
| Density |
8.44 g/cm³ |
| Melting Point |
1290 - 1350°C |
| Oxidation Resistance |
up to 982°C (1800°F) |
| Heat Treatment |
Solution annealed at 1093°C (2000°F) |
| Service Temperature Range |
196°C to 982°C |
| Specific Heat Capacity |
410 J/kg·K at 25°C |
| Applications |
Marine and offshore, Chemical processing, Heat exchangers |
|
Get IN-625 Alloy as per Standards Click Here
|
Table of Content
EOS Nickel Alloy IN625 Supplier in India, Refer Chemical Composition
Nickel Alloy IN625 Chemical Composition
| Element |
Min |
Max |
| Iron |
- |
5.00 |
| Silicon |
- |
0.50 |
| Manganese |
- |
0.50 |
| Sulfur |
- |
0.015 |
| Phosphorus |
- |
0.015 |
| Chromium |
20.0 |
23.0 |
| Titanium |
- |
0.40 |
| Cobalt |
- |
1.00 |
| Columbium + Tantalum |
3.15 |
4.15 |
| Aluminum |
- |
0.40 |
| Molybdenum |
8.00 |
10.0 |
| Carbon |
- |
0.10 |
| Nickel |
Bal. |
Mechanical Properties of Ni-Alloy IN625
| Aging Temperature, °F (°C) |
Aging Time, hrs. |
Average Charpy V-Notch Impact Strength |
| ft. lbs. |
J |
| Annealed** |
- |
81 |
110 |
| 1400 (760) |
1000 |
5 |
7 |
| 4000 |
4 |
5 |
| 8000 |
5 |
7 |
| 16000 |
4 |
5 |
| 1200 (649) |
1000 |
11 |
15 |
| 4000 |
8 |
11 |
| 8000 |
5 |
7 |
| 16000 |
4 |
5 |
| 1600 (871) |
1000 |
12 |
16 |
| 4000 |
11 |
15 |
| 8000 |
15 |
20 |
| 16000 |
14 |
19 |
Ni-Alloy IN625 Main Characteristics
- Combination of high strength
- Good corrosion resistance
- Oxidation resistance
- Good fabricability
Offer Japanese Origin IN-625 Alloy At Factory Price With Density 8.44 g/cm³ and Melting Point 1290 to 1350°C
IN-625 Alloy Physical Property
EOS NickelAlloy IN625 Process Information
| System Set-up |
EOS M 290 |
| EOSPAR name |
IN625_Performance M291 2.00 |
| Powder part no. |
|
| Software requirements |
-
EOSPRINT 2.5 or newer
- EOSYSTEM 2.5 or newer
|
| Recoater blade |
EOS HSS Blade |
| Nozzle |
EOS Grid Nozzle |
| Sieve |
63 µm |
| Inert gas |
Argon |
In 625 Alloy Aged Hardness at Room Temperature
| Aging Temperature, °F (°C) |
Aging Time, hrs. |
Average Charpy V-Notch Impact Strength |
| ft. lbs. |
J |
| Annealed** |
- |
81 |
110 |
| 1400 (760) |
1000 |
5 |
7 |
| 4000 |
4 |
5 |
| 8000 |
5 |
7 |
| 16000 |
4 |
5 |
| 1200 (649) |
1000 |
11 |
15 |
| 4000 |
8 |
11 |
| 8000 |
5 |
7 |
| 16000 |
4 |
5 |
| 1600 (871) |
1000 |
12 |
16 |
| 4000 |
11 |
15 |
| 8000 |
15 |
20 |
| 16000 |
14 |
19 |
In 625 Material Cutting Speeds for High-Speed Steels
| Operation |
Speed |
Feed |
| sfpm |
m/s |
ipr |
mm/rev |
| Drilling (0.500" / 12.70 mm) |
10-12 |
0.05 / 0.06 |
0.006 / 0.010 |
0.15 / 0.25 |
| Turning |
12-20 |
0.06 / 0.10 |
0.010 |
0.25 |
| Tapping |
5-10 |
0.03 / 0.05 |
- |
- |
| Reaming |
8-10 |
0.04 / 0.05 |
- |
- |
| Milling |
10-20 |
0.05 / 0.10 |
- |
- |
EOS Nickel Alloy IN625 Average Rupture Data
| Test Temperature, °F (°C) |
Average Rupture Strength, ksi (MPa) for Time Indicated |
| 10 hrs |
100 hrs |
1000 hrs |
| 1400 (760) |
36 (248) |
27 (186) |
20 (138)** |
| 1200 (649) |
82 (565) |
71 (490) |
60 (414) |
| 1600 (871) |
12 (83) |
6.7 (46) |
3.7 (26)** |
IN-625 Alloy Average Dynamic Modulus of Elasticity
| Form |
Condition |
Average Dynamic Modulus of Elasticity
psi × 10⁶ (MPa) |
Test Temp., °F (°C) |
| Plate, 3/8 in. (9.5 mm) thick |
Annealed at 1925°F (1052°C), rapid cooled |
30.2 (208,000) |
Room |
| 29.2 (201,000) |
200 (93) |
| 28.8 (199,000) |
400 (204) |
| 27.7 (191,000) |
600 (316) |
| 26.7 (184,000) |
800 (427) |
| 25.6 (176,000) |
1000 (538) |
| 24.3 (168,000) |
1200 (649) |
| 22.8 (157,000) |
1400 (760) |
| 21.2 (146,000) |
1600 (871) |
| 18.7 (129,000) |
1800 (982) |
Stockist Of Ni-Alloy IN625 in Mumbai For Aerospace Components and Marine Equipment
Ni-Alloy IN625 Applications
Stress Rupture Properties of In 625 Material
| - |
Stress[MPa] |
Time to Rupture
[h] |
Temperature[°C] |
Elongation[%] |
RA[%] |
| Vertical |
131 |
231 |
816 |
6.5 |
4.5 |
| Horizontal |
131 |
132 |
816 |
6.5 |
5 |
Buy In 625 Material Online in Different Forms With Service Temperature 1800°F, See Heat Treatment
| High Solution Anneal |
2000/2200°F (1093/1204°C) |
| Low Solution Anneal |
1700/1900°F (927/1038°C) |
| Stress Relieve |
1650°F (899°C) |
In625 High-Speed Cutting Tools for Lathe Turning Operations
| Angle |
Finishing |
Roughing |
| Back rake |
8° |
0° |
| Positive side rake |
14-18° |
- |
| End clearance |
8° |
6° |
| End cutting edge |
25° |
6° |
| Side cutting edge |
Up to 45° |
- |
Understand Difference Between In625 vs In718 Here
| Property |
Inconel 625 |
Inconel 718 |
| UNS |
N06625 |
N07718 |
| Density |
8.44 g/cm³ |
8.19 g/cm³ |
| Melting Point |
1290-1350°C (2350-2460°F) |
1260-1336°C (2300-2440°F) |
| Ultimate Tensile Strength |
930 MPa (135 ksi) |
1375 MPa (200 ksi) |
| Yield Strength (0.2% Offset) |
450 MPa (65 ksi) |
1100 MPa (160 ksi) |
| Elongation |
30-35% |
20-25% |
| Hardness (Rockwell C) |
Approx. 30 HRC |
Approx. 40 HRC |
| Modulus of Elasticity |
207 GPa (30 × 10⁶ psi) |
200 GPa (29 × 10⁶ psi) |
| Thermal Conductivity at 25°C |
9.8 W/m·K |
11.4 W/m·K |
| Electrical Resistivity |
1.29 × 10⁻⁶ Ω·m |
1.25 × 10⁻⁶ Ω·m |
In 625 Electrical Properties
| Electrical Resistivity |
0.000129 ohm-cm |
0.000129 ohm-cm |
| Magnetic Permeability |
1.0006 |
1.0006 |
| Curie Temperature |
Max -196 °C |
Max -321 °F |
Ni-Alloy IN625 Surface Roughness
| Horizontal surface |
Ra 1-5 µm |
| Vertical surface |
RA 1-5 µm |
In 625 Material Grades