| Incoloy Alloy 907 Spot Lights | |
|---|---|
| Heat Treatment |
|
| Material Type | Nickel-Iron-Cobalt Controlled Expansion Superalloy |
| UNS Designation | N19907 |
| Standard Specifications | ASTM B637, AMS 5829 |
| Service Temperature Range | -200°C to 650°C (-328°F to 1200°F) |
| Applications |
|
| Oxidation Resistance | up to 650°C (1200°F) |
| Creep Strength | up to 650°C (1200°F) |
| Electrical Resistivity | 72 μΩ·cm at 25°C |
| Specific Heat Capacity | 460 J/kg·K |
|
Get Nickel Alloy 907 as per Standards Click Here |
|
Table of Content
High Strength Incoloy 907 Supplier in India For Gas Turbines Components
| Temperature Range (°C) | Equivalent (×10⁻⁶ in/in·°F) | µm/m·°C |
|---|---|---|
| 20 - 100 | 7.0 | 12.6 |
| 20 - 200 | 7.2 | 13.0 |
| 20 - 400 | 7.3 | 13.2 |
| 20 - 600 | 7.5 | 13.5 |
- High strength and toughness at elevated temperatures
- Excellent oxidation and corrosion resistance
- Low thermal expansion and good fatigue resistance
- Maintains dimensional stability under thermal cycling
- Good weldability and fabricability
Buy UNS N19907 Material in Various Forms, Refer Chemical Composition
| Weight% | Ni | Ti | Al | Fe | Co | Nb | Si |
|---|---|---|---|---|---|---|---|
| Alloy 907 | 35.0-40.0 | 1.3-1.8 | 0.2 max | Bal | 12-16 | 4.3-5.2 | 0.07-0.35 |
| Heat Treatment Process | |
|---|---|
| Solution Annealing | 980°C (1800°F) |
| Age Hardening (Precipitation Treatment) | 720°C (1330°F) |
| Stress Relief | 600°C (1110°F) for 2 hours |
| Properties | Metric | English |
|---|---|---|
| Curie Temperature | 400 - 455 °C | 752 - 851 °F |
| Electrical Resistivity | 0.0000697 ohm-cm | 0.0000697 ohm-cm |
Stockist Of Inconel 907 in Mumbai With Density 8.33 g/cm3 and Melting Range 2440 - 2550 ° F
| Density | g/cm3 | 8.33 |
|---|---|---|
| lb/in.3 | 0.301 | |
| Melting Range | °F | 2440 - 2550 |
| °C | 1335 - 1400 | |
| Curie Temperature | °F | 750 - 850 |
| °C | 400 - 455 | |
| Specific Heat | Btu/lb-°F | 0.103 |
| J/kg-°C | 431 | |
| Electrical Resistivity | ohm circ mil/ft | 419 |
| μΩ-m | 0.697 | |
| Young’s Modulus (70°F) | 103 ksi | 23.9 |
| GPa | 165 | |
| Shear Modulus (70°F) | 103 ksi | 8.8 |
| GPa | 61 | |
| Poisson’s Ratio | 0.36 |
| Machining Parameter | Recommended Practice |
|---|---|
| Machinability Rating | Approximately 25% of free-cutting steel |
| Material Behavior During Machining | Tends to work harden quickly |
| Cutting Speed (High-Speed Steel Tools) | 18 - 25 m/min (60 - 80 ft/min) |
| Cutting Speed (Carbide Tools) | 50 - 70 m/min (160 - 230 ft/min) |
| Feed Rate (Roughing) | 0.10 - 0.20 mm/rev (0.004 - 0.008 in/rev) |
| Feed Rate (Finishing) | 0.05 - 0.10 mm/rev (0.002 - 0.004 in/rev) |
| Depth of Cut (Roughing) | 2.0 - 4.0 mm (0.08 - 0.16 in) |
| Depth of Cut (Finishing) | 0.25 - 1.0 mm (0.01 - 0.04 in) |
| Recommended Tool Material | Carbide (Grade C-2 or C-3) |
Offer Super Alloy 907 Material With Tensile Strength 1350 MPa At Fair Price, See Mechanical Properties
| Temperature | Yield Strength (0.2% Offset) |
Tensile Strength | Elongation | Reduction of Area | |||
|---|---|---|---|---|---|---|---|
| °F | °C | ksi | MPa | ksi | MPa | % | % |
| Age hardened for tensile-limited applications | |||||||
| 70 | 20 | 162.5 | 1120 | 194.5 | 1341 | 15.0 | 36.5 |
| 1200 | 649 | 126.2 | 870 | 151.2 | 1043 | 10.2 | 26.8 |
| 1400 | 760 | 82.0 | 565 | 93.9 | 647 | 20.9 | 52.0 |
| 800 | 427 | 142.4 | 982 | 168.3 | 1160 | 14.9 | 40.7 |
| 1000 | 538 | 137.5 | 948 | 164.3 | 1133 | 13.8 | 42.2 |
| Age hardened for rupture-limited applications | |||||||
| 70 | 20 | 128.5 | 886 | 175.5 | 1210 | 16.0 | 25.0 |
| 800 | 427 | 105.1 | 725 | 154.8 | 1067 | 16.6 | 32.6 |
| 1400 | 760 | 63.5 | 438 | 77.4 | 534 | 31.5 | 70.2 |
| 1000 | 538 | 105.5 | 727 | 150.2 | 1036 | 15.8 | 38.0 |
| 1200 | 649 | 98.7 | 681 | 136.5 | 941 | 19.8 | 42.2 |
| Properties | Metric | English |
|---|---|---|
| Specific Heat Capacity | 0.431 J/g-°C | 0.103 BTU/lb-°F |
| Thermal Conductivity | 14.8 W/m-K | 103 BTU-in/hr-ft²-°F |
| CTE, linear 20°C | 7.7 µm/m-°C | 4.28 µin/in-°F |
| CTE, linear 250°C | 7.7 µm/m-°C | 4.28 µin/in-°F |
| CTE, linear 500°C | 7.7 µm/m-°C | 4.28 µin/in-°F |
| Solidus | 1335 °C | 2430 °F |
| Liquidus | 1400 °C | 2550 °F |
Get Low Expansion Nickel Alloy 907 With Aged Hardened Condition, Check Modulus of Elasticity
| Temperature | Shear Modulus | Young’s Modulus | Poisson’s Ratio | |||
|---|---|---|---|---|---|---|
| °F | °C | 10³ ksi | GPa | 10³ ksi | GPa | |
| 70 | 21 | 8.8 | 61 | 23.9 | 165 | 0.36 |
| 200 | 93 | 8.7 | 60 | 23.8 | 164 | 0.37 |
| 400 | 204 | 8.7 | 60 | 23.8 | 164 | 0.37 |
| 600 | 316 | 8.9 | 61 | 24.0 | 165 | 0.35 |
| 700 | 371 | 9.0 | 62 | 24.1 | 166 | 0.34 |
| 800 | 427 | 9.1 | 63 | 24.3 | 167 | 0.34 |
| 900 | 482 | 9.0 | 62 | 24.2 | 167 | 0.34 |
| 1000 | 538 | 8.8 | 61 | 23.9 | 165 | 0.36 |
| 1200 | 649 | 8.2 | 56 | 22.4 | 155 | 0.36 |
| 1400 | 760 | 7.8 | 54 | 21.8 | 150 | 0.36 |
| 1600 | 871 | 7.4 | 51 | 20.5 | 141 | 0.39 |
- Work Hardening During Machining
- Moderate Machinability
- High Material Cost
- Requires Controlled Heat Treatment
- Limited Availability
- Welding Precautions Required
- Limited Data on Long-Term Creep