| Incoloy 909 High Lights | |
|---|---|
| Specifications |
|
| Material Type | Nickel-Iron-Cobalt Controlled Expansion Superalloy |
| Alloy Name | Incoloy 909 |
| Curie Temperature | 420°C (788°F) |
| Common Forms |
|
| Density | 8.14 g/cm³ |
| Melting Range | 1360 - 1390°C |
| Heat Treatment |
|
| Applications | Gas turbine shafts, aerospace bolts, precision instruments |
|
Get Nickel Incoloy 909 as per Standards Click Here |
|
Table of Content
High Strength Incoloy 909 Supplier in India With Low Thermal Expansion
| Property | Value |
|---|---|
| Coefficient of Thermal Expansion (20-100°C) | 11.9 µm/m·°C |
| Coefficient of Thermal Expansion (20-200°C) | 12.2 µm/m·°C |
| Coefficient of Thermal Expansion (20-400°C) | 12.5 µm/m·°C |
| Equivalent Expansion (20-400°C) | 6.9 × 10⁻⁶ in/in·°F |
| Thermal Stability Range | -200°C to +650°C (-328°F to +1200°F) |
| Temperature | Inflection Temperature - approximately 780°F (416°C) | ||
|---|---|---|---|
| °F | °C | 10⁻⁶/°F | 10⁻⁶/°C |
| 77 - 200 | 25 - 93 | 4.5 | 8.1 |
| 77 - 400 | 25 - 204 | 4.3 | 7.7 |
| 77 - 600 | 25 - 316 | 4.2 | 7.6 |
| 77 - 800 | 25 - 427 | 4.3 | 7.7 |
| 77 - 1000 | 25 - 538 | 5.0 | 9.0 |
- Low Thermal Expansion
- High Strength
- Outstanding Dimensional Stability
- Superior Oxidation Resistance
- Excellent Corrosion Resistance
- Good Weldability
- Thermal Stability
- Heat Treatable
Buy Inconel 909 Nickel Iron Cobalt Alloy For Gas Turbine Engine Components and Springs
| Properties | Metric | Imperial |
|---|---|---|
| Thermal expansion co-efficient (@ 20-427°C/68-801°F) | 7.70 µm/m°C | 4.28 µin/in°F |
| Thermal conductivity | 14.8 W/mK | 103 BTU.in/hr.ft².°F |
Stockist Of UNS N19909 Material in Mumbai With Good Corrosion and Fatigue Resistance, Refer Composition
| Weight% | Co | Nb | Si | Al | Ti | N | Fe | C |
|---|---|---|---|---|---|---|---|---|
| Alloy 909 | 12.0 - 16.0 | 4.3 - 5.2 | 0.25 - 0.50 | 0.15 max | 1.3 - 1.8 | 35.0 - 40.0 | Bal | 0.06 max |
| Properties | Metric | Imperial |
|---|---|---|
| Thermal conductivity | 14.8 W/mK | 103 BTU.in/hr.ft².°F |
| Thermal expansion co-efficient (@ 20-427°C/68-801°F) | 7.70 µm/m°C | 4.28 µin/in°F |
Offer Nickel Alloy 909 With Density 8.30 g/cm³ and Tensile Stength 1300 MPa, Check Mechanical Properties
| Material | Temperature | Tensile Strength | Yield Strength (0.2% Offset) | Reduction Area % | Elongation (%) | |||
|---|---|---|---|---|---|---|---|---|
| Ksi | MPa | Ksi | MPa | |||||
| Alloy 909 | 70F | 20C | 185 | 1276 | 150 | 1034 | 30 | 15 |
| 1200 | 650 | 150 | 1034 | 125 | 862 | 60 | 25 | |
| Density | 8.19 g/cm3 |
|---|---|
| Melting Temperature | 2606°F (1430°C) |
| Shear Modulus | 59 GPa |
| Young’s Modulus | 159 GPa |
| Curie Point | 851°F (455°C) |
- Cutting
- Drilling
- Turning
- Milling
- Grinding
Get Hot and Cold Worked Alloy 909 Which Heat Treated by Annealing Process At 983°C (1800°F)
| Solution Annealing | 980°C (1800°F) for 1 hour, air cool |
|---|---|
| Age Hardening | 720°C (1330°F) for 8 hours |
| Stress Relief | 600°C (1110°F) for 2 hours |