| IN939 Alloy Overview |
| Product Name |
Nickel-based IN939 |
| Common variants |
|
| Symbol |
IN939 |
| Composition |
IN939 |
| Particle Size |
15-45 um, 15-53 um, 45-105 um, etc. |
| Shape |
Spherical |
| Service Temperature |
850 °C (1,560 °F) |
| Heat Treatment |
High volume fraction (30-40%) |
|
Get In939 Material as per Standards Click
Here
|
Table of Content
Inconel 939 Material Supplier in India With Rupture Strength at Temperatures Up to 850
°c
Inconel 939 Material Rupture Strength
| Temperature |
Rupture Strength (MPa) |
| 700°C |
550 |
| 750°C |
500 |
| 800°C |
450 |
| 850°C |
400 |
| 900°C |
350 |
Ni-Alloy IN939 Material Data Sheet
| System set-up |
EOS M 290 |
| EOS MaterialSet |
IN939_040_HiPerM291_100 |
| Nozzle |
EOS Grid Nozzle |
| Powder part no. |
9011-0030 |
| Recoater blade |
EOS HSS Blade |
| Software requirements |
EOSPRINT 2.6 or newer
EOSYSTEM 2.10 or newer |
| Sieve |
63 µm |
| Inert gas |
Argon |
Inconel 939 Material Main Characteristics
- Excellent mechanical properties
- High tensile, fatigue, creep and rupture strength
- Maintains good ductility
- Crack-free in as-built condition and resistant
- Excellent corrosion and oxidation resistance
Offer EOS NickelAlloy IN939 Alloy Online For Industrial Gas Turbines and Instrumentation
Parts
EOS NickelAlloy IN939 Alloy Applications
Ni-Alloy IN939 Material Standards
| Specification |
Standards |
| ASTM |
ASTM B637 |
| ISO |
ISO 15156 |
| AMS |
AMS 5397 |
| UNS |
UNS N07090 |
Additional Information of In939 Alloy
| Property |
Value |
| Min. wall thickness |
Typical 0.3 - 0.4 mm |
| Volume rate |
3.6 mm³/s |
| Layer thickness |
40 µm |
Inconel 939 Alloy Powder Particle Size
| Spec. |
Particle Size |
Shape |
| IN939-DS045 |
15-45 um |
Spherical |
| IN939-DS053 |
15-53 um |
Spherical |
| IN939-DS105 |
45-105 um |
Spherical |
| IN939-DS150 |
45-150 um |
Spherical |
| Customizable |
Customizable |
Spherical |
IN939 Powder Thermal and Environmental Resistance
| Environment |
Service Temperature |
| Hot Corrosion |
980°C (1800°F) |
| Oxidizing |
1095°C (2000°F) |
| Aqueous Corrosion |
Excellent |
| Property |
Value |
Property |
Value |
| Mass density |
8.2 g/cm³ |
Thermal conductivity |
- |
| Particle size |
10 - 45 µm |
Particle shape |
Sphärisch |
Stockist Of Nickel-Chromium Alloy In939 Powder in Mumbai With Excellent Composition and
Mechanical Properties
| Element |
Value |
| W |
2.0 |
| Nb |
1.0 |
| Cr |
22.5 |
| Co |
19 |
| C |
0.15 |
| B |
0.01 |
| Ti |
3.7 |
| Al |
1.9 |
| Ta |
1.4 |
| Zr |
0.1 |
| Ni |
Balance |
Nickel-Chromium Alloy In939 Powder Mechanical Properties
| Property |
Value |
| Tensile Strength |
950 MPa |
| Yield Strength |
650 MPa |
| Elongation at Break |
15-20% |
IN939 Alloy Mechanical Properties in Heat Treated
Condition
| Direction |
Number of samples |
Ultimate tensile strength Rₘ [MPa] |
Yield strength Rₚ₀.₂ [MPa] |
Elongation at break A [%] |
| Vertical |
187 |
1,500 |
1,100 |
13 |
| Horizontal |
160 |
1,520 |
1,130 |
11 |
Buy Heat and Corrosion Resistant Ni-Alloy IN939 Material With Density 8.15 g/cm3
Ni-Alloy IN939 Physical Properties
| Property |
Value |
| Density |
8.19 g/cm³ |
| Melting Range |
1310°C - 1370°C |
Coefficient of Thermal Expansion ASTM E228
| Temperature |
25 - 100 °C |
25 - 400 °C |
25 - 200 °C |
25 - 800 °C |
25 - 600 °C |
25 - 900 °C |
| CTE |
12.18 × 10⁻⁶/K |
13.78 × 10⁻⁶/K |
12.89 × 10⁻⁶/K |
13.99 × 10⁻⁶/K |
13.49 × 10⁻⁶/K |
15.06 × 10⁻⁶/K |
Inconel 939 Surface Roughness of Downskin
Advantages of IN939 Powder
- High-Temperature Performance
- Excellent Oxidation and Corrosion Resistance
- Creep Resistance
- Versatile Manufacturing Capabilities
Find Source Of Tensile and Hardness Tested IN 939 Alloy With Solution and Aging Heat
Treatment
Ni-Alloy IN939 Material Heat Treatment
| Solution treatment |
Aging treatment |
| Hold at 1190 °C for 4 hours |
- Hold at 1000 °C for 6 hours
- Hold at 800 °C for 4 hours
|
Inconel 939 Material Hardness at room temperature ISO
6508
| Hardness, HRC |
Number of samples |
| 48 |
10 |
EOS NickelAlloy IN939 Roughness Measurement
| Roughness measurement |
As-built |
Corundum- and Glass-bead blasted |
Corundum blasted |
| M |
SD |
M |
SD |
M |
SD |
| Mean roughness depth (Rz) [µm] |
42 |
6 |
- |
- |
- |
- |
| Roughness average (Ra) [µm] |
6 |
1 |
- |
- |
- |
- |