| Inconel 792 High Lights | |
|---|---|
| Density | 8.1 g/cm³ |
| Specific Heat Capacity | 420-460 J/kg·K |
| Type | Austenitic standard |
| Class | High temperature corrosion Alloy steel |
| Category | High alloy steel |
| Finish | Mill Finish, Polished |
| Surface Treatment | Hot Rolled, Cold Rolled, Annealed |
| Alloy Type | Nickel-Chromium Alloy |
| Applications | Ornamental Applications |
| Common Trade Names | UNS C79200, CDA 792, C792, German Silver |
|
Get IN 792-5A Alloy as per Standards Click Here |
|
Table of Content
- Inconel 792 Superalloy Chemical Composition
- N792Mod.5A Material Equivalent
- Key Features of Inconel 792 Superalloy
- Inconel 792 Alloy Physical Properties
- IN 792-5A Alloy Rupture Strength
- Surface Treatment for Machined Inconel 792 Parts
- Inconel 792 Mod 5a Material Applications
- N792Mod.5A Cutting Parameters
- Alloy 792 Mechanical Properties
- Inconel 792 5a Surface Finishes
- Alloy 792 Tool Selection
- Inconel 792 Superalloy’s Machinability
- Alloy 792 Nickel-Chromium Alloy Heat Treatment
- Inconel 792 5A Electric Properties
- Alloy 792 Nickel-Chromium Alloy Thermal Properties
- CNC Machining Challenges for Inconel 792
IN 792-5A Cast Nickel-based Superalloy Supplier in India, Refer Chemical Composition
| Element | Percentage |
|---|---|
| Ni | 11 - 13 |
| Mn | 0 - 0.5 |
| Fe | 0 - 0.25 |
| Ni | 11 - 13 |
| Cu | 59 - 66.5 |
| Cu | 59 - 66.5 |
| Pb | 0.8 - 1.4 |
| Zn | 17.9 - 29.2 |
| Zn | 17.9 - 29.2 |
| Pb | 0.8 - 1.4 |
| Mn | 0 - 0.5 |
| Fe | 0 - 0.25 |
| Grade | Inconel 792 |
|---|---|
| ASTM | UNS N07792 |
| DIN | DIN 2.4856 |
| BS | Alloy 792 |
- High-Temperature Strength
- Superior Fatigue Resistance
- Corrosion Resistance
- Creep Resistance
- Versatile Industrial Application
Stockist Of High Temperature Strength Inconel 792 Alloy in Mumbai With Density 8.94 g/cm³
| Density | 0.303 lb/in3 |
|---|---|
| Melting Point | 1,660-1,750 °F |
| Specific Heat | 9.3 x 10^-2 BTU/lb-°F |
| Thermal Conductivity | 288 BTU-in/hr-ft^2-°F |
| Electrical Conductivity | 28% IACS |
| Properties | Metric | English |
|---|---|---|
| Rupture Strength |
|
|
|
|
|
|
|
|
|
|
- Hot Isostatic Pressing (HIP)
- Thermal Barrier Coating (TBC)
- Electrical Discharge Machining (EDM)
- Deep Hole Drilling
Get Creep Resistance Inconel 792 Mod 5a Material For Jet Engine Blades and Gas Turbine Parts
| Operation | DOC (mm) | Feed (mm/rev) | Speed (m/min) | Coolant Pressure (bar) |
|---|---|---|---|---|
| Roughing | 2.0-3.0 | 0.20-0.30 | 15-25 | 80-100 |
| Finishing | 0.3-0.8 | 0.05-0.10 | 30-45 | 100-150 |
Buy Polished and Mill Finish Inconel 792 5a Suitable to Work At 1000°C, Check Mechanical Properties
| Yield Tensile Strength | 73 ksi |
|---|---|
| Ultimate Tensile Strength | 79 ksi |
| Shear Modulus | 6,400 ksi |
| Shear Strength | 45 ksi |
| Elongation at Break Percentage | 3.6% |
| Modulus of Elasticity | 17,400 ksi |
| Poisson's Ratio | 0.32 |
- Polished
- Mill Finish
- Machined Finish
- Ground Finish
- Shot-Peened Surface
- Lapped Finish
| Parameter | Recommendation |
|---|---|
| Coating | AlTiN, AlCrN (3-6 µm) |
| Tool Material | PVD-coated carbide or SiAlON ceramics |
| Geometry | Positive rake (10-12°), edge honed for strength |
- Vacuum Investment Casting
- Single Crystal Casting
- Equiaxed Crystal Casting
- Superalloy Directional Casting
- Powder Metallurgy Turbine Disc
- Superalloy Precision Forging
- CNC Machining
- Hot Isostatic Pressing (HIP)
Find Source Of Hot and Cold Rolled Alloy 792 Nickel-Chromium Alloy in Various Forms, View Heat Treatment
| Heat Treatment | Temperature |
|---|---|
| Annealing | 845 °C |
| First Ageing | 1080 °C |
| Second Ageing | 845 °C |
| Solution Treatment | 1120 °C |
| Critical Eutectic Point | 1230 °C |
| Carbide Solution Point | 1260 °C |
| Properties | Conditions | ||
|---|---|---|---|
| T (°C) | Treatment | ||
| Electric Resistivity (10-9W-m) | 690 | 25 | 25 |
| Properties | Conditions | ||
|---|---|---|---|
| T (°C) | Treatment | ||
| Thermal Expansion (10-6/ºC) | 17.5 | 0-100 more | |
| Thermal Conductivity (W/m-K) | 16.2 | 100 more | |
| Specific Heat (J/kg-K) | 500 | 0-100 | |
- Elevated Hardness and γ′ Strengthening
- Heat Retention and Built-up Edge
- Abrasive Carbides and Intermetallics