| Nickel Alloy 263 Overview | |
|---|---|
| Designations |
|
| Specifications |
|
| Hardness | 28.0 HRC |
| Sub-Group | Superalloy |
| Machinability | 18% |
| Material Group | S - Superalloys (Heat resistant and Titanium) |
| Common Trade Names | Nimonic C263® |
| Standard Inventory Specifications | UNS N07623, AMS 5872 |
| Other industry standards | B50A774, W.Nr. 2.4650 |
| Common Applications |
|
| Suitable welding filler materials | 2.4650 |
|
Get Alloy 263 as per Standards Click Here |
|
Table of Content
- UNS N07263 Physical Properties
- Insert Cutting Edge Geometry for Material Nimonic C263
- Nicrofer 5120 CoTi Machining Properties
- Alloy 263 Material Chemical Composition
- Nimonic 263 Alloy Equivalent
- Cutting Speeds Recommendations for Material Nimonic C263
- Nickel Alloy 263 Heat Treatment
- Nimonic 263 Material Thermal Properties
Most Trusted UNS N07263 Supplier in India With Density 8.36 g/cm³
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.36 g/cm³ | 0.302 lb/in³ |
| Melting point | 1300-1355°C | 2370-2471°F |
| Honing Size: | 0.02-0.05 mm / 0.001-0.002" |
|---|---|
| Land Width: | 0.10-0.20 mm / 0.004-0.008" |
| Rake Angle: | 13° -18° |
| Land Angle: | Neutral |
| Ground Insert: | Recommended |
- Tool Selection
- Cutting Speed
- Feed Rate
- Depth of Cut
- Coolant Use
- Tool Geometry
- Workpiece Fixturing
- Tool Wear Monitoring
Buy Alloy 263 Material At Best Price, Refer Chemical Composition and Equivalent
| Element | Content (%) |
|---|---|
| Cobalt, Co | 19-21 |
| Chromium, Cr | 19-21 |
| Molybdenum, Mo | 5.60-6.10 |
| Titanium, Ti | 1.90-2.40 |
| Iron, Fe | 0.70 |
| Manganese, Mn | 0.60 |
| Aluminum, Al | 0.60 |
| Silicon, Si | 0.40 |
| Nickel, Ni | 49 |
| Copper, Cu | 0.20 |
| Carbon, C | 0.040 - 0.080 |
| Boron, B | 0.0050 |
| Sulfur, S | 0.0070 |
| Standard | Name |
|---|---|
| WNR | 2.4650 |
| DIN | NiCr20CoMoTi |
| UNS | UNS N07263 |
| BS | HR10 |
| AFNOR | NCK20D |
| Application | Vc (SFM) | Vc (m/min) |
|---|---|---|
| Turning | 200-280 | 60-85 |
| Milling | 150-200 | 45-60 |
| Parting | 130-160 | 40-50 |
| Grooving | 180-230 | 55-70 |
| Drilling | 150-200 | 45-60 |
Top WNR 2.4650 Stockist in Mumbai With Solution Annealed at 1149°C (2100°F) , See Heat Treatment
| Solution Treatment | 1150 °C |
|---|---|
| Ageing Treatment | 800 °C |
| Properties | Metric | Imperial |
|---|---|---|
| Thermal conductivity | 11.7 W/mK | 81.2 BTU in/hr.ft².°F |
| Thermal expansion co-efficient (@21-100°C/69.8-212°F) | 10.3 µm/m°C | 5.72 µin/in°F |
Get Haynes® 263 With Tensile Strength 940 MPa and Hardness up to 28 HRC , View Mechanical Properties
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 940 MPa | 136000 psi |
| Yield strength | 550 MPa | 79800 psi |
| Elongation at break | 39% | 39% |
| Temperature Range (°C) | Coefficient of Linear Thermal Expansion (CTE) ×10⁻⁶ /°C |
|---|---|
| 20-100 | ≈ 10.3 |
| 20-200 | ≈ 11.9 |
| 20-300 | ≈ 12.5 |
| 20-400 | ≈ 13.1 |
| 20-500 | ≈ 13.6 |
- Drilling
- Turning
- Milling
- Grinding
Offer Nickel Alloy 263 For Aircraft Turbine Engine and Land-based Turbine Applications
| Welding Requirement | Details |
|---|---|
| Welding Method | Preferred: GTAW/TIG; Optional: GMAW/MIG with precautions. |
| Filler Material | Use Nimonic 263 filler wire/rod |
| Preheat | Typical preheat: 200°C-400°C (392°F-752°F) |
| Welding Parameters | Adjust current, voltage, and travel speed to avoid excessive heat input. |
| Shielding Gas | Use high-purity argon |
- High Temperature Strength
- Creep Resistance
- Oxidation and Corrosion Resistance
- Good Weldability
- High Fatigue Resistance
- Formability
- Durability
| Form | Typical Stock Sizes | How Weight is Calculated |
|---|---|---|
| Round bar | Ø 6 mm → Ø 200 mm (stockists vary) | length × π × (Ø/2)² × density |
| Plate | 0.5 mm → 60 mm (thickness) | area × thickness × density |
| Tube | OD/ID by wall thickness | tube volume = π × (OD² − ID²)/4 × length × density |
| Forging blanks | As required | custom mass per forging design |
- Round
- Flats
- Extruded Section
- Tube
- Plate
- Sheet
- Wire
Get in touch
Call
+91-22-6639 4858
Email