| Nimonic Alloy PE16 Overview |
| Machining |
- Turning, Parting Off
- Grooving, Milling Indexable
|
| Material Group |
S - Superalloys (Heat resistant and Titanium) |
| Sub-Group |
Superalloy |
| Hardness |
100.0 HRB |
| Tensile Strength |
810 [N/mm^2] |
| Machinability Range |
15% - 45% |
| Density |
8.2 g/cm³ |
| Melting range |
1320-1380 °C |
| Used |
Turbine engines, Aerospace components |
|
Get Alloy PE16 as per Standards Click Here
|
Table of Content
Nimonic Alloy PE16 Supplier in India With Service Temperature 500-750°c, Refer Composition
Nimonic Alloy PE16 Chemical Composition
| % |
Ni+Co |
Mo |
Cu |
Co |
C |
Mn |
Cr |
Si |
S |
Ti |
Al |
Zr |
B |
| Min |
42 |
2.8 |
0 |
0 |
0.04 |
0 |
15.5 |
0 |
0 |
1.1 |
1.1 |
0.02 |
0 |
| Max |
45 |
3.8 |
0.5 |
2 |
0.08 |
0.2 |
17.5 |
0.5 |
0.015 |
1.3 |
1.3 |
0.04 |
0.005 |
BS HR207 Temprature Range
| Specification |
Temperature Range (°C) |
| Service Temperature |
500 - 750 |
| Upper Limit |
≈ 750 |
Nimonic Alloy PE16 Creep-Rupture Properties
| Solution treated and then aged 1 h /900°C/AC + 8 h/750°C/AC |
| °C |
Stress, MPa, to produce rupture in |
Elongation at fracture on 5.65√So % |
| 300 h |
1000 h |
3000 h |
10 000 h |
| 700 |
301 |
255 |
217 |
178 |
21-28 |
| 650 |
- |
363 |
332 |
285 |
13-20 |
| 750 |
185 |
155 |
128 |
100 |
13-27 |
Get Nickel Alloy PE16 With Good Strength and Oxidation Resistance At Reasonable Price
AFNOR NW 11 AC Key Features
- Good ductility
- High-temperature capability
- Oxidation & creep resistance
- Fabricability and versatility
- Wide industrial applicability
- High strength
Nimonic PE16 Total Plastic Strain Data
| Solution treated and then aged 1 h/900°C/AC + 8 h/750°C/AC |
| Test Temperature °C |
Strain, % |
Stress, MPa, to give total plastic strain in |
| 100 h |
300 h |
1000 h |
3000 h |
10 000 h |
| 750 |
0.1 |
132 |
116 |
89 |
70 |
53 |
| 0.2 |
151 |
131 |
108 |
86 |
64 |
| 0.5 |
162 |
145 |
124 |
105 |
85 |
| 1.0 |
170 |
153 |
131 |
113 |
92 |
| 700 |
0.1 |
209 |
185 |
155 |
132 |
- |
| 0.2 |
239 |
209 |
178 |
148 |
115 |
| 0.5 |
263 |
231 |
201 |
170 |
137 |
| 1.0 |
279 |
247 |
209 |
185 |
155 |
| 650 |
0.1 |
332 |
293 |
255 |
217 |
(170) |
| 0.2 |
355 |
317 |
279 |
239 |
201 |
| 0.5 |
386 |
347 |
309 |
271 |
231 |
| 1.0 |
394 |
355 |
317 |
285 |
247 |
Stockist Of BS HR55 Material in Mumbai Ideal For Nuclear Reactors and Gas-Turbines Components
NIMONIC® Alloy PE16 Applications
Super Alloy Nimonic PE16™ Physical Properties
| Density |
Mg/m3 |
8.00 |
| lb/in3 |
0.289 |
| Melting Range |
|
| Liquidus Temperature |
°C |
1355 |
| Solidus Temperature |
°C |
1310 |
| Specific Heat |
(20-400°C), J/kg·°C |
544 |
AFNOR NW 11 AC Dynamic Moduli
| °C |
Dynamic Torsional Modulus (GPa) |
Dynamic Young's Modulus (GPa) |
| 20 |
74 |
198 |
| 100 |
73 |
193 |
| 200 |
71 |
187 |
| 300 |
69 |
180 |
| 400 |
66 |
175 |
| 500 |
62 |
168 |
| 600 |
59 |
161 |
| 700 |
55 |
153 |
| 800 |
53 |
144 |
| 900 |
48 |
134 |
| 1000 |
42 |
122 |
Cutting Speeds for Heat resistant Ni or Co Based PE16 Alloy
| Application |
Vc (SFM) |
Vc (m/min) |
| Milling |
150-440 |
45-135 |
| Parting |
130-380 |
40-115 |
| Turning |
200-590 |
60-180 |
| Grooving |
180-520 |
55-160 |
| Drilling |
180-520 |
55-160 |
Buy AFNOR NW 11 AC Alloy in Various Form With Density 8.98 g/cm³, Check Mechanical Properties
AFNOR NW 11 AC Alloy Mechanical Properties
| Material |
Condition 20°C |
Tensile Strength MPa |
0.2 % Proof Stress MPa |
Reduction of Area % |
Elongation % |
| PE16 |
Heat Treatment 2h/1040°C/AC +2h 800°C/AC + 16/700°C/AC |
880 |
525 |
54 |
37 |
| Heat Treatment 4h/1040°C/AC + 1h 900°C/AC + 8h/750°C / AC |
830 |
450 |
55 |
29 |
Alloy PE16 Thermal Conductivity and Electrical Resistivity
| °C |
Thermal Conductivity W/m °C |
Electrical Resistivity at 20°C = 1.1 MΩm |
| Relative Resistance |
| 20 |
11.72 |
1.000 |
| 200 |
15.07 |
1.047 |
| 300 |
16.75 |
1.073 |
| 100 |
13.82 |
1.022 |
| 700 |
23.03 |
1.132 |
| 800 |
25.12 |
1.129 |
| 400 |
18.42 |
1.094 |
| 500 |
19.68 |
1.109 |
| 600 |
21.35 |
1.121 |
| 900 |
26.80 |
1.129 |
| 1000 |
28.47 |
1.139 |
Nimonic PE16 Mean Coefficient of Linear Thermal Expansion
| °C |
µm/m · °C |
| 20-200 |
14.6 |
| 20-300 |
14.9 |
| 20-400 |
15.1 |
| 20-500 |
15.5 |
| 20-900 |
18.0 |
| 20-100 |
13.8 |
| 20-600 |
16.0 |
| 20-700 |
16.4 |
| 20-800 |
17.2 |
| 20-1000 |
18.5 |
Offer Precipitation Hardened BS HR207 Nickel Iron Chromium With Various Heat Treatment
PE16 Material Heat Treatment
| Heat Treatment |
Temperature (°C) |
| Solution Treatment |
1040 |
| Aging - Option A |
900 |
| 750 |
| Aging - Option B |
800 |
| 700 |
BS HR207 Impact Values, J, at Room Temperature
| Soaking time (h) |
Soaking Temperature, °C |
| 500 |
600 |
650 |
700 |
800 |
| 3000 |
- |
75 : 79 |
46 : 48 |
35 : 29 |
57 : 54 |
| 10 000 |
117 : 102 |
57 : 62 |
34 : 52 |
26 : 29 |
58 : 61 |
| 300 |
110 : 111 |
91 : 94 |
81 : 85 |
79 : 71 |
106 : 110 |
| 1000 |
96 : 95 |
84 |
65 : 64 |
54 : 52 |
80 : 60 |
| 30 |
133 : 109 |
103 : 98 |
95 : 98 |
98 : 100 |
128 : 125 |
| 100 |
110 : 104 |
95 : 90 |
88 : 95 |
88 : 84 |
123 : 117 |
Nimonic Alloy PE16 Impact Values, J, at Elevated Temperature
| Soaking time (h) |
Soaking and Test Temperature, °C |
| 500 |
600 |
650 |
700 |
800 |
| 3000 |
- |
62 : 73 |
57 : 49 |
50 : 52 |
65 : 75 |
| 10 000 |
106 : 109 |
65 : 62 |
58 : 56 |
46 : 38 |
84 : 79 |
| 300 |
95 : 96 |
80 : 77 |
71 : 72 |
73 : 71 |
111 : 103 |
| 1000 |
95 : 92 |
72 : 71 |
60 : 60 |
62 : 66 |
84 : 91 |
| 30 |
95 : 100 |
100 : 92 |
76 |
81 : 81 |
109 : 114 |
| 100 |
109 : 103 |
80 : 87 |
76 : 76 |
76 : 79 |
113 : 110 |
Nimonic PE16 Superalloy’s Machinability
- Vacuum Investment Casting
- Single Crystal Casting
- Equiaxed Crystal casting
- Superalloy Directional Casting
- CNC Machining
- Superalloy Welding
Equivalent International Designations for Material Nimonic PE16
| Standard |
Name |
| BS |
HR207 |
| DIN |
NiFe33Cr17Mo |
| ANFOR |
NW11AC |
Recommended Insert Cutting Edge Geometry for Material Nimonic PE16
| Honing Size |
0.02-0.05 mm / 0.001-0.002" |
| Land Width |
0.10-0.20 mm / 0.004-0.008" |
| Rake Angle |
13° -18° |
| Land Angle |
Neutral |
| Ground Insert |
Recommended |