| Nickel Cobalt Alloy Udimet 500 High Lights |
| Heat treatment |
- Normalizing,Annealing
- Tempering,Quenching
|
| Mchining |
- Turning, Milling
- Grinding, Deep hole drilling
|
| Material Group |
S - Superalloys (Heat resistant and Titanium) |
| Sub-Group |
Superalloy |
| Tensile Strength |
[N/mm^2] |
| Machinability Range |
15% - 45% |
| Specific Heat |
420-450 J/kg·K |
| Service Temperature |
Up to ~760-870 °C |
| Thermal Conductivity |
11-14 W/m·K |
Get Udimet 500 Alloy as per Standards Click Here
|
Table of Content
Top UNS N07500 Material Supplier in India, See Chemical Composition
UNS N07500 Material Chemical Composition
| Element |
Amount |
| Chromium (Cr) |
19% |
| Iron (Fe) |
4.0% |
| Silicon (Si) |
0.1% |
| Nickel (Ni) |
52% |
| Cobalt (Co) |
18% |
| Molybdenum (Mo) |
4% |
| Titanium (Ti) |
3% |
| Aluminum (Al) |
3% |
| Carbon (C) |
0.07% |
| Manganese (Mn) |
0.1% |
Equivalent International Designations for Material Udimet 500
| Standard |
Name |
| UNS |
UNS N07500 |
| ANFOR |
NCK19DAT |
| SAE |
AlSl 684 |
| WNR |
2.4983 |
| DIN |
NiCr18CoMoAlTi |
Nickel Cobalt Alloy Udimet 500 Key Features
- High Temperature Strength
- Outstanding Creep Resistance
- Good Oxidation Resistance
- High Hardness & Wear Resistance
- Good Hot Corrosion Resistance
- Good Hot-Workability
Buy Udimet 500 Special Metals For High Temperature Applications Like Gas Turbine Blades
Super Alloy Udimet 500™ Applications
Cutting Speeds for Heat resistant Ni or Co Based Udimet 500
| Application |
Vc (SFM) |
Vc (m/min) |
| Turning |
200-590 |
60-180 |
| Milling |
150-440 |
45-135 |
| Parting |
130-380 |
40-115 |
| Grooving |
180-520 |
55-160 |
| Drilling |
180-520 |
55-160 |
Nickel Cobalt Alloy Udimet 500 Heat Treatment
| Annealing |
Tempering |
Normalizing |
Quenching |
Q & T |
| √ |
√ |
√ |
√ |
√ |
Recommended Insert Cutting Edge Geometry for Material Udimet 500
| Honing Size |
0.02-0.05 mm / 0.001-0.002" |
| Land Angle |
Neutral |
| Land Width |
0.10-0.20 mm / 0.004-0.008" |
| Rake Angle |
13° -18° |
| Ground Insert |
Recommended |
High Strength UNS N07500 Super Alloy Stockist in Mumbai Which Annealed At 1079°C (1975°F) , Refer Equivalent
UNS N07500 Super Alloy Heat Treatment
| Heat Treatment |
Temperature |
| Solution Treatment |
1080-1120 °C |
| Stabilization Treatment |
~845-870 °C |
| Age Hardening |
700-760 °C |
| Stress Relief |
650-700 °C |
Size Availability for Super Alloy Udimet 500™
| Steel Grade |
Specification |
Processing range(mm) |
| Udimet 500 Stainless Steels |
Round Bar and Hollow Bar |
Φ1 to Φ2000 |
| Square and Flat Steel |
Φ10 to Φ100 |
| Plate and Sheet |
0.08-800(Thickness)*10-1500(Width)*Length |
| Tube or Pipe |
OD:Φ4-410; WT:1-35 mm; Lenght:10-12000 |
| Coil and Strip Steel |
THK:0.1mm Width:1500mm |
| Forged |
Ring/Cylindrical/Disk |
Offer Precipitation Hardening WNR 2.4983 Nickel-Base Superalloy With Density 8.5 g/cm³, See Properties
Nickel Cobalt Alloy Udimet 500 Mechanical Properties
| Tensile strength
Rm (MPa) |
Proof strength
Rp0.2 (MPa) |
Impact energy
KV (J) |
Reduction in cross section on fracture
Z (%) |
Elongation at fracture
A (%) |
Brinell hardness (HBW) |
As-Heat-Treated Condition |
| 685 (≥) |
245 (≥) |
12 |
42 |
14 |
412 |
Solution and Aging, Annealing, Ausaging, Q+T,etc |
Udimet 500 Nickel-Base Superalloy Various Forms
| Products |
Dimension |
Processes |
| Plates / Sheets |
0.08-200mm(T)*W*L |
Forging, hot rolling and cold rolling |
| Steel Coil /Steel Strip |
0.03-16.0x1200mm |
Cold-Rolled & Hot-Rolled |
| Round Bar, Flat Bar, Square Bar |
Φ8-1200mm*L |
Forging, hot rolling and cold rolling, Cast |
| Seamless Pipes/Tubes, Welded Pipes/Tubes |
OD:6-219mm x WT:0.5-20.0mm |
Hot extrusion, Cold Drawn, Welded |
Get DIN NiCr18CoMoAlTi in Various Forms like Plate, Round Bar, Pipe etc. Check Physical Properties
WNR 2.4983 Nickel-Base Superalloy Physical Properties
| Property |
Temperature T
°C/F |
Density
kg/dm3 |
Electric resistance
µΩ·cm |
Specific heat
J / kgK |
Thermal conductivity
W/mK |
Modulus of elasticity
kN/mm2 |
Expansion rate |
| 874 (≥) |
43 |
797 (≥) |
Solution and Aging, Annealing, Ausaging, Q+T,etc |
11 |
13 |
241 |
241 |
| Temp.
°C/°F |
Creep rupture strength
(10000h)
(Rp1,0) N/mm2 |
Creep strain limit
(10000h)
(Rp1,0) N/mm2 |
- |
- |
- |
- |
- |
| 844 |
192 |
123 |
- |
- |
- |
- |
- |
Udimet 500 Nickel Alloy Powder Advantages
- High sphericity
- Low oxygen
- Smooth surface
- Uniform particle size distribution
- Excellent flow properties
- High purity
Deliver Status of Udimet 500 Alloy
| Product type |
Deliver Status |
| Steel Bar |
Black, Rough Turning, Shot Blasting, |
| Plates / Sheets |
Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes |
Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Coil / Strip |
Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |