| Udimet 700 Alloy Data Sheet |
| Heat Treatment |
- Solution Annealing: 1020 - 1060 °C
- Age Hardening: 700 - 760 °C
|
| Specific Heat |
435 J/kg·K |
| Material Group |
S - Superalloys (Heat resistant and Titanium) |
| Sub-Group |
Superalloy |
| Tensile Strength |
[N/mm^2] |
| Machinability Range |
15% - 45% |
| Modulus of Rigidity |
82 GPa |
| Category |
High alloy steel |
| Class |
High temperature corrosion Alloy steel |
| Common Names |
Chromium-Manganese-Udimet 700 |
| Designations |
ASTM, UNS, AISI, DIN EN, DIN SEW, ISO, JIS, NF, BS, GB. |
|
Get Udimet 700 as per Standards Click Here
|
Table of Content
AISI 687 Supplier in India At Fair Price, See Chemical Composition
Udimet 700 Alloy Chemical Composition
| Component Elements Properties |
Metric |
English |
| Boron, B |
0.03 % |
0.03 % |
| Carbon, C |
0.07 % |
0.07 % |
| Chromium, Cr |
15.09 % |
15.09 % |
| Cobalt, Co |
18.5 % |
18.5 % |
| Iron, Fe |
<= 1.0 % |
<= 1.0 % |
| Molybdenum, Mo |
5.0 % |
5.0 % |
| Aluminum, Al |
4.3 % |
4.3 % |
| Nickel, Ni |
53 % |
53 % |
| Titanium, Ti |
3.4 % |
3.4 % |
ANFOR NCKD20AT Rupture Strength
| Propertie |
Metric |
English |
| Rupture Strength |
- 55.2 MPa
- @Temperature 982 °C,
- Time 3.60e+6 sec
|
- 8000 psi
- @Temperature 1800 °F,
- Time 1000 hour
|
- 117 MPa
- @Temperature 982 °C,
- Time 360000 sec
|
- 17000 psi
- @Temperature 1800 °F,
- Time 100 hour
|
- 296 MPa
- @Temperature 816 °C,
Time 3.60e+6 sec
|
- 43000 psi
- @Temperature 1500 °F,
- Time 1000 hour
|
- 400 MPa
- @Temperature 816 °C,
- Time 360000 sec
|
- 58000 psi
- @Temperature 1500 °F,
- Time 100 hour
|
- 703 MPa
- @Temperature 649 °C,
- Time 3.60e+6 sec
|
- 102000 psi
- @Temperature 1200 °F,
- Time 1000 hour
|
Equivalent International Designations for Material Udimet 700
| Standard |
Name |
| SAE |
AlSl 687 |
| WNR |
2.4636 |
| DIN |
NiCo15Cr15MoAlTi |
| AFNOR |
NCKD20AT |
Buy WNR 2.4636 Wrought Nickel-Base Alloy With Density 8.25gm/cm3
Physical Properties of Udimet 700 Alloy
| Property |
Density
kg/dm3 |
Temperature T
°C/F |
Thermal conductivity
W/mK |
Specific heat
J / kgK |
Modulus of elasticity
kN/mm2 |
Electric resistance
µΩ·cm |
| 595 (≥) |
141 (≥) |
44 |
44 |
43 |
132 |
Solution and Aging, Annealing, Ausaging, Q+T,etc |
WNR 2.4636 Thermal Conductivity
| Properties |
Metric |
English |
| Thermal Conductivity |
- 19.7 W/m-K
- @Temperature 20.0 - 100 °C
|
- 136 BTU-in/hr-ft²-°F
- @Temperature 68.0 - 212 °F
|
SAE Udimet 700 Superalloys Thermal Properties
| Properties |
Conditions |
| T (°C) |
Treatment |
| Thermal Expansion (10-6/ºC) |
17.5 |
0-100 more |
- |
| Specific Heat (J/kg-K) |
500 |
0-100 |
- |
Cutting Speeds for Heat resistant Ni or Co Based AlSl 687
| Application |
Vc (SFM) |
Vc (m/min) |
| Turning |
200-590 |
60-180 |
| Milling |
150-440 |
45-135 |
| Parting |
130-380 |
40-115 |
| Grooving |
180-520 |
55-160 |
| Drilling |
150-440 |
45-135 |
SAE Udimet 700 Superalloys Creep Properties
| Temp.
°C/°F |
Creep strain limit
(10000h)
(Rp1,0) N/mm2 |
Creep rupture strength
(10000h)
(Rp1,0) N/mm2 |
| 268 |
715 |
823 |
Offer DIN NiCo15Cr15MoAlTi Material With Machinability Range 15% to 45%, Refer Mechanical Properties
DIN NiCo15Cr15MoAlTi Material Mechanical Properties
| Properties |
Conditions |
| T (°C) |
Treatment |
| Tensile Strength (Mpa) |
515 |
25 |
annealed (sheet, strip) more |
| Yield Strength (Mpa) |
275 |
| Elongation (%) |
40 |
| Reduction in Area (%) |
- |
| Poisson's Ratio |
0.27-0.30 |
25 |
- |
| Elastic Modulus (GPa) |
190-210 |
25 |
- |
AISI 687 Electric Properties
| Properties |
Conditions |
| T (°C) |
Treatment |
| Electric Resistivity (10-9W-m) |
690 |
25 |
- |
Trusted ANFOR NCKD20AT Stockist in Mumbai in Various Form At Discounted Price
ANFOR NCKD20AT Various Form
| Product Type |
Forms |
Dimension |
| Steel Bar |
Round Bar, Flat Bar, Square Bar |
Φ8-1200mm*L |
| Plates / Sheets |
Plates / Sheets |
0.08-200mm(T)*W*L |
| Pipes / Tubes |
Seamless Pipes/Tubes, Welded Pipes/Tubes |
OD:6-219mm x WT:0.5-20.0mm |
| Coil / Strip |
Steel Coil /Steel Strip |
0.03-16.0x1200mm |
Recommended Insert Cutting Edge Geometry for Material Udimet 700
| Honing Size: |
0.02-0.05 mm / 0.001-0.002" |
| Land Width: |
0.10-0.20 mm / 0.004-0.008" |
| Rake Angle: |
13° -18° |
| Land Angle: |
Neutral |
| Ground Insert: |
Recommended |
Benefits of Udimet 700 Alloy
- Excellent High-Temperature Strength
- Superior Creep Resistance
- High Stress-Rupture Strength
- Stable Microstructure
- Versatility in Applications
- Good Weldability and Fabrication
Find SAE Udimet 700 Alloy Online Most Ideal For Turbine Disks and Blades in Jet Engines
SAE Udimet 700 Alloy Applications
Udimet 700 Surface Finish Chart by Machining Technology
| Machining Process |
Ra [Micro Inches] |
Ra [Micrometers] |
| 3D Printing |
125 |
3.1 |
| Drilling |
63 |
1.6 |
| Milling |
32 |
0.8 |
| Turning |
16 |
0.4 |
| Grinding |
4 |
0.1 |
| Lapping |
2 |
0.1 |
Deliver Status for DIN NiCo15Cr15MoAlTi
| Product Type |
Processes |
Deliver Status |
| Steel Bar |
Forging, hot rolling and cold rolling, Cast |
Black, Rough Turning, Shot Blasting, |
| Plates / Sheets |
Forging, hot rolling and cold rolling |
Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes |
Hot extrusion, Cold Drawn, Welded |
Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Coil / Strip |
Cold-Rolled & Hot-Rolled |
Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |