| Udimet 710 Spot Lights |
| Heat Treatment |
- Solution Treatment: 2100°F
- Aging Treatment: 1950°F
|
| Material Group |
S - Superalloys (Heat resistant and Titanium) |
| Sub-Group |
Superalloy |
| Tensile Strength |
[N/mm^2] |
| Machinability Range |
15% - 45% |
| Specific Heat |
450-500 J/kg·K |
| Service Temperature |
Up to ~750-800 °C |
| Electrical Resistivity |
1.2-1.4 μΩ·m |
| Hardness |
350-400 HV |
|
Get Super Alloy Udimet 710™ as per Standards Click Here
|
Table of Content
Super Alloy Udimet 710™ Supplier in India With Density 8.276 g/cm³
Super Alloy Udimet 710™ Physical Properties
| Properties |
Value |
Unit |
| Density |
7700 - 7700 |
kg/m³ |
| Melting temperature |
1450 - 1510 |
°C |
| Thermal expansion |
10 - 10 |
e-6/K |
| Thermal conductivity |
25 - 25 |
W/m·K |
| Specific heat |
460 - 460 |
J/kg·K |
| Resistivity |
0.55 - 0.55 |
Ohm·mm²/m |
Equivalent International Designations for Material Udimet 710
| Standard |
Name |
| AFNOR |
NCK18TDA |
Udimet 710 Alloy Key Features
- High strength at elevated temperatures
- Good creep and creep-rupture resistance
- Good oxidation and corrosion resistance
- Heat treatable
- Thermal stability and structural integrity
- Good fabricability
Offer Material Udimet 710 With Good Oxidation and Creep Resistance in Variety of Shapes
Material Udimet 710 Processing Range
| Shapes |
Processing Range (mm) |
| Round bar |
Φ1 to Φ2000 |
| Square-shape steel/Flate bar |
10 to 1000 |
| Steel Plate/Sheet |
0.08 to 800(T) * 10 to 1500(W) * Long |
| Forging |
Pipe/tube/slugs/donuts/cubes/other shapes |
| Tubings |
OD: Φ4-410; WT: 1-35 mm |
| Steel coils and strip |
THK: 0.1 mm Width: 1500 mm |
Super Alloy Udimet 710™ Rupture Strength
| Properties |
Metric |
English |
| Rupture Strength |
- 68.9 MPa
- @Temperature 982 °C,
- Time 3.60e+6 sec
|
- 10000 psi
- @Temperature 1800 °F,
- Time 1000 hour
|
- 121 MPa
- @Temperature 980 °C,
- Time 360000 sec
|
- 17500 psi
- @Temperature 1800 °F,
- Time 100 hour
|
- 131 MPa
- @Temperature 982 °C,
- Time 360000 sec
|
- 19000 psi
- @Temperature 1800 °F,
- Time 100 hour
|
- 331 MPa
- @Temperature 816 °C,
- Time 3.60e+6 sec
|
- 48000 psi
- @Temperature 1500 °F,
- Time 1000 hour
|
- 469 MPa
- @Temperature 816 °C,
- Time 360000 sec
|
- 68000 psi
- @Temperature 1500 °F,
- Time 100 hour
|
Material Udimet 710 Charpy V Notch Impact
| Alloy |
As-Heat Treated (Kg·m) |
After 10,000 hr at 871°C (Kg·m) |
| U710 |
2.22 |
0.55 |
Phases Present in Udimet 710 After Heat Treatment and Exposure to Elevated Temperature
| Specimen |
X-ray Intensity |
| MC |
M23C6 |
MC : M23C6 |
Other |
| As heat treat |
15 |
3 |
5:1 |
Boride + ? |
| 1500/1000 hr |
5 |
10 |
1:2 |
Boride or σ ? |
| 1500/2000 hr |
2 |
9 |
1:4.5 |
1 1/2 σ ? |
| 1600/1000 hr |
3.5 |
13 |
1:3.7 |
Boride or σ ? |
| 1600/2000 hr |
1.5 |
11 |
1:7.3 |
1 σ ? |
| 1700/1000 hr |
1 |
16 |
1:16 |
? |
| 1700/2000 hr |
0.25 |
15.5 |
1:62 |
- |
| 1800/1000 hr |
0.5 |
17 |
1:34 |
? |
| 1800/2000 hr |
0.25 |
19 |
1:76 |
- |
| 1900/100 hr |
5 |
13.5 |
1:27 |
- |
| 2000/100 hr |
MC only present |
| 2100/10 hr |
MC only present |
| 2200/10 hr |
MC only present (4.31 Å) |
Time-Temperature for Phase Stability Determination of Udimet 710
| Exposure Temp, °F |
Exposure Time, Hours |
| 1 Hour |
10 Hours |
100 Hours |
500 Hours |
1000 Hours |
2000 Hours |
| 1500 |
- |
- |
- |
X |
X |
X |
| 1600 |
- |
- |
- |
X |
X |
X |
| 1700 |
- |
- |
- |
X |
X |
X |
| 1800 |
- |
- |
- |
X |
- |
X |
| 1900 |
- |
X |
X |
- |
- |
- |
| 2000 |
X |
X |
X |
- |
- |
- |
| 2100 |
X |
- |
- |
- |
- |
- |
| 2200 |
X |
- |
- |
- |
- |
- |
Stockist Of Udimet 710 Alloy in Mumbai Which Annealed at 1177°C (2150°F)
Heat Treatment for Udimet 710 Alloy
| Treatment |
Temperature |
Duration |
| Solution Treatment |
2100°F |
2 hours |
| Aging Treatment |
1950°F |
4 hours |
| Aging Treatment |
1400°F |
16 hours |
Cutting Speeds for Heat resistant Ni or Co Based Udimet 710
| Application |
Vc (SFM) |
Vc (m/min) |
| Turning |
200-590 |
60-180 |
| Milling |
150-440 |
45-135 |
| Parting |
130-380 |
40-115 |
| Grooving |
180-520 |
55-160 |
| Drilling |
150-440 |
45-135 |
Refer ANFOR NCK18TDA Material Chemical Composition and Mechanical Properties
ANFOR NCK18TDA Material Chemical Composition
| Element |
Value |
| Cobalt (Co) |
15% |
| Titanium (Ti) |
5% |
| Aluminum (Al) |
2.5% |
| Nickel (Ni) |
55% |
| Chromium (Cr) |
18% |
| Molybdenum (Mo) |
1.5% |
| Iron (Fe) |
0.5% |
| Carbon (C) |
0.07% |
Mechanical Properties of Udimet 710 Alloy
| Specimen |
Test Temp, °F |
0.2% YS ksi |
UTS ksi |
Reduction of Area % |
% Elong in 1 in. |
| As heat treat |
RT |
130.1 |
158.9 |
10.9 |
11.2 |
| 1600/2000 hr |
RT |
97.6 |
129.6 |
9.5 |
7.6 |
| 1600/2000 hr |
RT |
98.0 |
122.0 |
6.9 |
7.9 |
| As heat treat |
1400 |
112.5 |
149.5 |
14.7 |
16.4 |
| 1600/2000 hr |
1400 |
85.5 |
112.2 |
6.0 |
7.7 |
| 1600/2000 hr |
1400 |
89.8 |
118.6 |
6.9 |
8.0 |
Super Alloy Udimet 710™ Applications
Buy Udimet 710 With Different Welding Method like GTAW, GMAW and MIG etc.
Udimet 710 Welding Methods
| Welding Methods |
| GTAW |
Gas Tungsten Arc Welding |
| GMAW |
Gas Metal Arc Welding |
| MIG |
Metal Inert Gas Welding |
Electron Vacancy Calculation Results for ANFOR NCK18TDA
| Nv Number |
Ht 5245 |
Spec. Max. |
Spec. Min. |
| Nvₛₛ |
2.49 |
2.66 |
2.33 |
| Nv₁* |
2.58 |
2.79 |
2.40 |
| Nv₂* |
2.63 |
2.87 |
2.44 |
| Nv₃* |
2.33 |
2.48 |
2.20 |
| Nv₄* |
2.37 |
2.54 |
2.23 |
| Nv₅* |
2.49 |
2.66 |
2.33 |
| Nv₆* |
2.53 |
2.73 |
2.36 |
| Nv₉ |
2.94 |
3.16 |
2.64 |
Recommended Insert Cutting Edge Geometry for Material Udimet 710
| Honing Size: |
0.02-0.05 mm / 0.001-0.002" |
| Land Width: |
0.10-0.20 mm / 0.004-0.008" |
| Rake Angle: |
13° -18° |
| Land Angle: |
Neutral |
| Ground Insert: |
Recommended |
Material Udimet 710 Weight Gain
| Material |
Weight Gain [mg/cm2] |
| 900 °C/8 h |
900 °C/48 h |
900 °C/96 h |
| Udimet 710 |
−2.04 ± 0.08 mg/cm2 |
4.25 ± 0.17 mg/cm2 |
44.34 ± 1.77 mg/cm2 |