| Udimet 80 Alloy Spot Lights |
| Specifications |
- ASTM B637
- BS 3076 NA 20, BS HR 1, BS HR 601
|
| Heat Treatment |
- Annealed: 1080 - 1120 °C
- Spring Temper: 600 °C
- Age-Hardened: 700 °C
|
| Material Group |
S - Superalloys (Heat resistant and Titanium) |
| Specific Heat |
420 - 448 J/kg·K |
| Density |
8.19 g/cm³ |
| Maximum Continuous Service Temperature |
815 °C |
| Applications |
Gas turbine components, Nuclear industry |
| Electrical Resistivity |
1.08 - 1.09 µΩ·m |
| Sub-Group |
Superalloy |
| Machinability |
12% |
|
Get Udimet 80 Special Metals as per Standards Click Here
|
Table of Content
Best Nicrofer 7520 Ti Supplier in India, Refer Chemical Composition
Nicrofer 7520 Ti Chemical Composition
| Element |
Min % |
Max % |
| S |
- |
0.015 |
| Ag |
- |
0.0005 |
| Al |
1.00 |
1.80 |
| B |
- |
0.008 |
| Bi |
- |
0.0001 |
| Co |
- |
2.00 |
| Cr |
18.00 |
21.00 |
| C |
0.04 |
0.10 |
| Si |
- |
1.00 |
| Mn |
- |
1.00 |
| Cu |
- |
0.20 |
| Fe |
- |
1.50 |
| Pb |
- |
0.002 |
| Ti |
1.8 |
2.70 |
Material Udimet 80 Mechanical Properties
| Property |
Value |
| Yield Strength (0.2% offset, room temp) |
750 - 760 MPa |
| Ultimate Tensile Strength (room temp) |
1180 - 1200 MPa |
| Elongation (room temp, age-hardened) | 20 - 45% |
| Hardness (as-hardened, typical room temp) |
250 - 350 HB |
| High-Temperature / Creep / Rupture Strength |
Usage up to ~815 °C |
| Continuous Service Temperature (typical) |
Up to ~815 °C in air |
Udimet 80 Nickel-Base Superalloy Key Features
- High-Temperature Strength
- Creep and Stress-Rupture Resistance
- Oxidation and Corrosion Resistance
- Heat-Treatable
- Good Fatigue Resistance
- Fabrication and Workability
- Dimensional Stability
Stock and Supply Pyromet 80A Material For Gas Turbine Components and Nuclear Industry
Pyromet 80A Material Applications
Recommended Tool Types for Milling Nicrofer 7520 Ti
- Solid Carbide End Mill
- Coated Carbide Mill
- Face Mill
Milling Parameters for Udimet 80 Alloy
| Parameter |
Recommended Value |
| Cutting Speed (m/min) |
20-40 |
| Feed Rate (mm/tooth) |
0.05-0.2 |
| Depth of Cut (mm) |
1.5-4 |
Udimet 80 Coefficient of Thermal Expansion
| Temperature Range (°C) |
Coefficient of Thermal Expansion (µm/m·°C) |
| 20 - 100 |
~12.7 |
| 20 - 200 |
~13.3 |
| 20 - 300 |
~13.7 |
| 20 - 500 |
~14.4 |
| 20 - 700 |
~15.5 |
| 20 - 800 |
~16.2 |
Stockist Of Superimphy 80A in Mumbai With Density 8.19 g/cm³ and Melting Point 1365 °C
Superimphy 80A Physical Properties
| Property |
Value |
|---|
| Density | 8.19 g/cm³ |
| Melting |
1320 - 1365 °C |
| Specific Heat (at ~20 °C) | 420 - 448 J/kg·K |
| Thermal Conductivity (at ~20-100 °C) |
11.2 - 11.4 W/m·K |
| Coefficient of Linear Thermal Expansion (CTE) |
~12.7 µm/m·°C (20-100 °C) |
| Modulus of Elasticity (Young’s) |
190 - 200 GPa |
| Modulus of Rigidity (Shear modulus) | 85 kN/mm² |
| Electrical Resistivity |
1.08 - 1.09 µΩ·m at 20 °C |
Pyromet 80A Stress-Rupture Strength
| Temperature |
Stress-Rupture Strength |
| 600°C |
600 MPa |
| 650°C |
520 MPa |
| 700°C |
440 MPa |
| 760°C |
220 MPa |
| 815°C |
130 MPa |
Udimet 80 Special Metals Modulus Properties
| Modulus of Rigidity |
Modulus of Elasticity |
| 85 kN/mm² |
222 kN/mm² |
| 12328 ksi |
32199 ksi |
Buy Super Alloy Udimet 80™ Alloy With Annealed and Spring Temper Condition, Check Heat Treatment
Super Alloy Udimet 80™ Alloy Heat Treatment
| Conditions |
Heat Treatment |
| Annealed Condition |
- Solution anneal: 1080°C - 1120°C
- Hold time: 1-2 hours
• Cooling: Air cool
|
| Spring Temper Condition |
-
Age harden: 600°C for 16 hours
- Cooling: Air cool
|
| Standard Age-Hardened Condition |
-
Age harden: 700°C for 16 hours
- Cooling: Air cool
|
Recommended Tool Types for Turning Superimphy 80A
| Tool Type |
Coating Type |
| Carbide Tool |
TiN (Titanium Nitride) |
| Ceramic Tool |
Al2O3 (Alumina) |
| CBN (Cubic Boron Nitride) |
- |
Offer Udimet 80 Nickel-Base Superalloy Suitable to Work At Temperature Range 800 °C (1,472 °F)
Udimet 80 Nickel-Base Superalloy Temperature Services
| Services |
Temperature |
| Maximum Continuous Service Temperature |
Up to ~815°C (1500°F) |
| Intermittent Service Temperature |
Up to ~870°C (1600°F) |
| Optimal Creep-Resistant Range |
650°C - 815°C |
| Maximum Oxidation-Resistant Range |
700°C - 900°C |
| Recommended Working Range |
600°C - 800°C |
Turning Parameters for Material Udimet 80
| Parameter |
Recommended Value |
| Cutting Speed (m/min) |
30-50 |
| Feed Rate (mm/rev) |
0.1-0.3 |
| Depth of Cut (mm) |
1-5 |